1. Hasi - roller grafite ikarito yikarito kugirango imikorere ikorwe
Ibikorwa nyamukuru byakazi bya silikoni yicyuma ikarito: ikoreshwa mumatanura ya annealing hamwe nubushyuhe ntarengwa bwa dogere 1000, ikirere cya hydrogène ya azote nikirere cyuzuye.
2.Ibipimo bya tekiniki nibisabwa kubisabwa munsi ya roller ya grafite ya karubone
))
2.)
|
抗折强度 |
Biruta cyangwa bingana na 25MPa |
GB / T3074.1-2008 |
|
Imbaraga zo guhonyora |
Birarenze cyangwa bingana na 40MPa |
GB / T1431-2009 |
|
Ubucucike bwinshi |
Kurenza cyangwa bingana na 1.74g / cm3(ibicuruzwa byarangiye) |
|
|
Ibirimo ivu |
Ntabwo ari munsi cyangwa bingana na 0.2% |
GB / T1429-2009 |
|
Gukomera ku nkombe |
Birarenze cyangwa bingana na 35 (ibicuruzwa byarangiye) |
|
|
Ubwoba |
Umubare ntarengwa Ntarengwa cyangwa ungana na 1.0mm, ubujyakuzimu Ntabwo buri munsi cyangwa bingana na 1.0mm, ubwinshi Ntabwo buri munsi cyangwa bingana na 10 / igice |
|
|
Kurwanya |
Ntibiri munsi cyangwa bingana na 9.5Ωμm |
YB / T120-1997 |
|
Fe + ibirimo |
Ntabwo ari munsi cyangwa bingana na 0.50 ％ |
|
|
Ca + ibirimo |
Ca + 含量 Ntibisanzwe cyangwa bingana na 0.30 ％ |
|
|
Ibirimo alkaline |
Ntibiri munsi cyangwa bingana na 0.10 ％ |
|
|
Coefficient yo kwagura ubushyuhe |
Ntibiri cyangwa bingana na 2.5 × 10-6/ impamyabumenyi |
GB / T3074.4-2003 |
|
Ubuso bukabije |
Intego y'agaciro Ra1.6 |
|
|
Ibisabwa |
Ntibiri munsi cyangwa bingana na dogere 1000, ikirere cyuzuye |